32CrMo12-forged-round-bar

32CrMo12 / 1.7361 Steel – EN 10250

32CrMo12 / 1.7361 steel is a nitriding steel which has at least 2.8Cr%,0.3%Mo as strengthening elements as per EN10250 standard.Similar with 30CrMo12,31CrMo12, it has a high tensile strength 880 – 1230 MPa after QT. 32CrMo12 / 1.7361 has high surface hardness and wear resistance after nitrided,but this material is difficult to weld and should therefore not be used in welded constructions.

32CrMo12 / 1.7361 Steel Supply Form & Size & Tolerance

Hot rolled round bar:Φ20-Φ120mm,Length:3000-9000mm

Hot Forged round bar:Φ130-Φ1000mm,Length:3000-10000mm

Flat bar/Blcoks:Thickness :120-800mm xWidth:120-1500mm,Length:2000-6000mm

Surface Finish Black-Forged Black-Rolled Turned Grinding Polished Peeled Cold Drawn
Tolerance (0,+5mm) (0,+1mm) (0,+3mm) Best h9 Best h11 Best H11 Best H11

32CrMo12 / 1.7361 Steel Chemical Composition per EN 10250-3

GRADE NUMBER C Si Mn P S Cr Mo Ni
32CrMo12 1.7361 0.28-0.35 ≤ 0.40 0.40-0.70 ≤ 0.035 ≤ 0.035 2.80-3.30 0.30-0.50 ≤ 0.60

 

32CrMo12 / 1.7361 Steel Relevant Standards

Europe France UK Sweden
31CrMo12/1.8515 30CD12 722M24 2240

32CrMo12 / 1.7361 Steel Mechanical Property

Thickness of ruling section T,mm ≤160 160-330 ≥330
Yield Strength Mpa ≥680 ≥630 ≥490
Tensile Strength Mpa ≥900 ≥850 ≥700
Elongation, % longitudinal ≥12 ≥13 ≥15
transverse ≥8 ≥9 ≥11
Impact,J longitudinal ≥35 ≥35 ≥35
transverse ≥20 ≥20 ≥20

32CrMo12 / 1.7361 Steel Physical Property

  • Density: 7.8 g/cm3
  • Mean coefficient of expansion in m/m.°C:
    – between 20 °C and 100 °C:11.3 x 10-6
    – between 20 °C and 500 °C:13.6 x 10-6
  • Critical points:
    – Ac 1: 780 °C
    – Ac 3: 835 °C
  • Modulus of elasticity :210GMpa

32CrMo12 / 1.7361 Steel Forging

32CrMo12 / 1.7361 Steel forging temperature:900 – 1100°C ,cooling as slowly as possible in sand after forged.

32CrMo12 / 1.7361 Steel Heat Treatment

  • Normalizing:  880 – 920°C,Cooling in air
  • Soft Annealing:650 – 700°C,Cooling in furnace,Hardness:max 248 HB
  • Hardening:890 – 940°C,water or oil quench
  • Tempering:550 – 740°C,Cooling in air
  • Nitriding: 480-570°C. Hardness after nitridng is 480-570 HV1.

32CrMo12 / 1.7361 Steel Application

32CrMo12 / 1.7361 Steel is used in automotive and general mechanical engineering components which requires high hardness and wear resistance,also suitable for gear wheels, cylinders, drills, connecting rods, shafts, extruders, quides, thread gauges with relatively large-cross section.