20mncr5 mat 1.7147 steel round bars

20MnCr5 / 1.7147 Steel

20MnCr5/1.7147  Alloy steel manufacturers and suppliers, supplied in round rods,square/flat bars,rollers,shafts,blocks and forging pieces.

20MnCr5/1.7147  Alloy steel  a Chromium-Manganese steel according to DIN standard which has tensile strength and wearing resistance after QT heat treatment.It is widely used in piston bolts, spindles, camshafts, gears, shafts and other mechanical controlling parts.

20MnCr5 / 1.7147 Steel Chemical Composition per EN 10084 (Case Hardening Steel)

GRADE NUMBER C Si Mn P S Cr
20MnCr5 1.7147 0.17-0.22 ≤ 0.40 1.10-1.40 ≤ 0.025 ≤ 0.035 1.00-1.30

20MnCr5 / 1.7147 Steel Mechanical Property

Tensile strength Yield strength Elongation Reduction of area
1400Mpa 1200MPa 13 57

20MnCr5 / 1.7147 Steel Related Specifications

DIN AFNOR BS ASTM/SAE
16MnCr5 16MC5 590M17 5115
20MnCr5 20MC5 5120

20MnCr5 / 1.7147 Steel Heat Treatment & Mechanical Property

20MnCr5/20MnCrS5
Normalizing,°C 840-870
Annealing,°C 650-700
Carburizing,°C 880-980
Core Hardening,°C 860-900
Case Hardening,°C 780-820
Tempering,°C 150-200

20MnCr5 / 1.7147 Steel Hardness requirements for delivery conditions

Conditions 16MnCr5/16MnCrS5 20MnCr5/20MnCrS5
Treated to improve shearability(+S) ≤255
Soft annealed(+A) ≤207 ≤217
Treated to Hardness range(+TH) 156-207 170-217
Treated to ferrite-pearlite structure and hardness range(+FP) 140-187 152-201
Normalized(+N) 138-187 140-201

20MnCr5 / 1.7147 Steel Hardenability Limits

Distance from quenched end mm 1.5 3.0 5.0 7.0 9.0 11 13 15 20 25 30 35 40
16MnCr5+H
16MnCrS5+H
Min 39 36 31 28 24 21
Max 47 46 44 41 39 37 35 33 31 30 29 28 27
20MnCr5+H
20MnCrS5+H
Min 41 39 36 33 30 28 26 25 23 21
Max 49 49 48 46 43 42 41 39 37 35 34 33 32
16MnCr5+HH
16MnCrS5+HH
Min 42 39 35 32 29 26 24 22 20
Max 47 46 44 41 39 37 35 33 31 30 29 28 27
20MnCr5+HH
20MnCrS5+HH
Min 44 42 40 37 34 33 31 30 28 26 25 24 23
Max 49 49 48 46 43 42 41 39 37 35 34 33 32
16MnCr5+HL
16MnCrS5+HL
Min 39 36 31 28 24 21
Max 44 43 40 37 34 32 30 28 26 25 24 23 22
20MnCr5+HL
20MnCrS5+HL
Min 41 39 36 33 30 28 26 25 23 21
Max 46 46 44 42 39 37 36 34 32 30 29 28 27

20MnCr5 / 1.7147 Steel Supply Form & Size

  • Round Bars:  Dia.80 – 1,000mm as Forged
  • Flat / Square Bars:  Thickness Max.800mm
  • Shafts, Rollers, Blocks:  Customized or According to Drawing
  • Rolled Round Bars:  Dia.16 – 130mm with UT Assurance

Heat treatment: Normalizing (+N), Annealing (+A)
Surface finish:Black / Rough turned / Peeled

20MnCr5 / 1.7147 Steel – The Comprehensive FAQ Guide

If you’ve been in the steel industry for quite some time now, then you know the importance and the significance of the 20NbCr5 or 1.7147 steel.

Should you be unsure of what it is, you’re just on the right page! In this FAQ guide, we will be waking you through what 20MnCr5 or 1.7417 steel is. Moreover, we will also help you identify it from other types of steel that are the closest.

By the end of this particular guide, you will be an expert in determining the 1.7417 or 20MnCr5 steel manufacturer you should work with.

What is 20MnCr5 Material?

It is a type of steel that’s casehardened that contains lower levels of carbon content.

what is 20mncr5 material
Image of what 20MnCr5 material looks like in round bars

Moreover, you can also expect it to have decent levels of hardenability as well as wear resistance and ductility.

Its composition has an alloying element, which is chromium, and you have the option to harden and make it stronger up to a total hardness level of HRC 41.

This particular steel type is the most ideal for parts and components that are required to be at a strength level of 1,000 to 1,300 N/mm2.

What is Case Hardening?

Case hardening simply is a material processing methodology you would want to use to increase and heighten the hardness level of a certain material for the outer surface of it.

what is case hardening
Case hardening of steel

Performing case hardening would most likely result to a thin layer of metal that is harder and tougher than the metal volume below the hardened layer.

Basically, it’s a process that helps produce a wear-resistant surface all the while maintaining strength and toughness at the core of a material.

What Can You Use 20MnCr5 / 1.7145 Steel For?

20mncr5 mat 1.7147 steel round bars
Stacks of round bars of 20MnCr5 / 1.7147 steel

To name a few of the most customary applications you can use 20MnCr5 / 1.7147 steel for include:

  • Camshafts
  • Shafts
  • Gears
  • Spindles
  • Piston Bolts
  • Boxes
  • Mechanical Controlling Parts
  • And Many More!

Thanks to its good-to-moderate wear resistance, you can find many uses for 20MnCr5 steel no matter what type of industry and sector you are in!

You can use 20MnCr5 steel to make and create goods where the surface of it is subject to thermochemical or thermal treatment. In addition to that, you can find it suitable for engineering and mechanical parts!

Is 20MnCr5 and 5120 Steel the Same?

5120 steel is one of 20MnCr5’s equivalent materials; 20MnCr5 is from China, while 5120 steel is from the United States (U.S.).

is 20mncr5 and 5120 steel the same
Thin example of 5120 steels

They are equivalent materials, however, it doesn’t necessarily mean that they share identical alloying element content.

What is C35 Steel?

C35 steel is a type of steel that contains medium level of carbon content.

what is c35 steel
C35 steel in round bars

Unlike 20MnCr5, C35 is a moderate-level carbon steel that you can use for a wide array of applications, but mostly, it’s for the parts and components of machines and equipment.

It boasts of its excellent state of being forged, machinability, and weldability.

20MnCr5 vs. 16MnCr5 Material

The most common misconception that people have with 20MnCr5 and 16MnCr5 is that they’re just the same.  And while they’re both alloyed steels for case hardening, they’re not actually the same.

20MnCr5 is a steel grade that is low-alloyed. In the same way, 16MnCr5 falls under the same category.

16MnCr5 is a type of steel that contains carbon levels that range between 0.14 and 0.19%, while 20MnCr5 has about 0.17 to 0.22%. This difference in carbon is actually big, especially because of the fact that carbon is the main component in contributing to the hardness or the toughness of the steel.

While that is the case, 20MnCr5 and 16MnCr5 are similar in terms of normalizing, annealing, and carburizing.

What is EN31 Steel?

EN31 steel is a type of steel that has high levels of strength. In addition to that, EN31 is a type of steel alloy that you would harden and temper before supplication.

what is en31 steel
Raw EN31 round bar steels

Furthermore, EN31 steel is a type of steel that contains too few alloying elements such as molybdenum (Mn), chromium (Cr), nickel (Ni), and more. These elements are what makes the wear resistance, tensile strength, durability, and ductility at its peak!

The base hardness of EN31 steel is at 24 HRC, which is typically at the moderate-to-low hardness compared to its counterparts.

What Are Equivalent Materials of the 20MnCr5 / 1.7417 Steel?  

The equivalent materials and steels of 20MnCr5 or 1.7417 steels include:

  • USA – 5120
  • Germany – 1.7417
  • Japan – SMnC420H

What Are the Mechanical Properties of 20MnCr5 / 1.7147 Steel?

The mechanical properties are the physical properties of the steel wherein it shows its capabilities when forces are applied.

It is imperative to be aware of the mechanical properties of steels before deciding on them, why? – Because you can consider that as your basis on whether or not the steels will be able to fit your needs and requests.

20MnCr5 or 1.7147 Steel’s Mechanical Properties

  • Tensile Strength: 520 MPa
  • Yield Strength: 415 MPa (Minium)
  • Bulk Modulus: 140 GPa
  • Shear Modulus: 80 GPa
  • Thermal Conductivity: 46.6 W/mK

8620 Steel and What is it Used For?

From the designation of the steel alone, you would know that it’s not a type of steel that’s made and manufactured in China.

8620 steel and what it is used for
Example of what 8620 steel looks like

It’s a standard that’s been made and created in the U.S. Furthermore, it is a low-carbon type of case-hardening steel that contains various alloying elements, wherein its base include nickel, chromium, and molybdenum.

Similar to that of 20MnCr5 / 1.7147 steel, you can use the 8620 alloy to produce and manufacture parts and components that have good levels of wear resistance, including ring gears, crankshafts, shafts, fasteners, enclosures, and many more!

It shares almost the same properties to the USA counterpart of 20MnCr5 or 1.7147 steel, it just contains added alloying elements in the process.

20MnCr5 Material Price

Determining the price of 20MnCr5 / 1.7147 is difficult – or rather quite impossible. What you might get online might not be accurate and precise, causing you to have problems with the budget.

The best thing to do in this case is to contact and ask a particular 20MnCr5 / 1.7147 manufacturer. More often than not, they will grant you a free estimate or a free quote.

In addition to that, if you’re going to purchase 20MnCr5 steel wholesale, you will be able to get better and more considerable rates and prices for it.

So, never assume that all manufacturers and suppliers will ask for the same price. Have the expectation that it will always be different.

20MnCr5 Steel Composition

Knowing what a particular steel grade is comprised of will be one of the best and the most essential things to figure out if a particular steel grade is for you.

Here’s a table of the chemical composition of the 20MnCr5 / 1.7147 steel:

Carbon (C) Chromium (Cr) Manganese (Mn) Phosphorus (P) Sulfur (S) Silicon
0.17 to 0.22% 1.00 to 1.30% 1.10 to 1.40% ≤0.035% ≤0.035% ≤0.4%

With this table, you can easily recognize and distinguish whether or not 20MnCr5 / 1.7147 steel is the type of steel for you.

To help you further with what each of these alloying elements contribute to the overall steel, they are:

Chromium

Having chromium means that a particular material’s rusting or oxidation-resistance levels are more and are better. This happens because instead of the steel surface oxidizing, the chromium oxidizes first and will form a protective layer of the steel.

Manganese

The more manganese a steel has, the harder, stronger, and the more durable it is. The major downside of having high levels of manganese is the fact that it’ll have a slower rate of quenching.

Phosphorus

Phosphorus contributes to the strength and hardness of a particular steel or material. If your steel has high levels of phosphorus, you can expect it to have increased hardness, strength, and an enhanced machinability.

Silicon

What Silicon (Si) does on steels is that it increases both the yield and the tensile strength. Due to this, the forgeability, hardness, as well as the permeability of the steel is enhanced and developed, too.

Sulfur

Sulfur decreases the weldability of a particular steel, while it develops the machinability. Sulfur is carefully added onto steels because if it’s added without enough levels of manganese, it’ll become less ductile, less tough, and it’ll produce red heat brittleness.

Those are the primary alloying elements that 20MnCr5 / 1.7147 steel has, but that’s not the complete list of alloying elements present. There are others and there are a lot more!

What is the HRC Hardness of 20MnCr5 / 1.7417 Steel?

The HRC hardness that 1.7417 / 20MnCr5 steels can reach up to a maximum of 60 to 66 via salt-bath furnace and oil quenching.

However, if you choose to have it air-cooled, it can arrive at an HRC hardness levels that range between 22 and 30 HRC.

Can You Trust 20MnCr5 / 1.7417 Chinese Steel Manufacturers?

Yes, there are a lot of businesses that trust and rely on 20MnCr5 or 1.7417 Chinese steel manufacturers.

As a matter of fact, most of them are from the West like the Americas or Europe. Getting in work with a Chinese manufacturer of 20MnCr5 steel is like getting the best and the highest quality you can get in the cheapest and the most affordable rates.

20MnCr5 Steel Supply Forms

What type of shapes, forms, and sizes can you purchase 20MnCr5 or 1.7147 steel in? Supply forms, for the benefit of everyone, are the forms or shapes you can purchase a specific steel or metal in.

Akin to other types of steel, you can purchase 20MnCr5 / 1.7147 steel in many different supply forms and shapes. The most common ones include, but are not limited to:

  • Round Bars or Round Steels
  • Sheet Steels
  • Square Bars or Square Steels
  • Plates

But, of course you can always opt to go with custom 20MnCr5 / 1.7147 steel if you want all of your products to be specific to whatever your business needs are!

One good tip before choosing a manufacturer is to ask them if they’re offering 20MnCr5 / 1.7147 steel that can be custom-made or specific to the needs of clients. 9 times out 10, they’ll agree to it, however, there are some that don’t.

It’s always better to be safe than sorry!

Which Chinese 1.7417 or 20MnCr5 Steel Supplier Should You Trust?

Out of all the many Chinese 20MnCr5 suppliers in the market, we here at Waldun Steel are deemed and considered to be the best and the most trusted.

Waldun Steel has been considered to be the epitome of excellence when it comes to steel manufacturing. Apart from 20MnCr5 or 1.7417 steel, you can also count on us to help you with other steel types and grades, such as AISI 4140 alloy steel, AISI 1020 carbon steels, EN 41B nitriding steels 30CrNiMo8 / 1.6580 steel, and many more!

There’s no limit as to what you can get when you choose Waldun Steel as your manufacturer!

Why Work With Waldun Steel?

Apart from us being the best, the most experienced, and the most skilled, we’re also the 20MnCr5 / 1.7147 steel manufacturer that you can trust because all of our equipment and machinery have undergone extreme tests.

In addition to that, our company is also equipped with the most advanced technologies and calibration processes, guaranteeing you nothing but higher-quality 20MnCr5 steel products for the most affordable and commendable rates.

Get a Free Quote!

Don’t worry about how much budget you’ll need because we wouldn’t make you guess. Waldun Steel will already give you the estimate or the quotation that you need!

Contact us today by dialing our hotline or by giving us a call! We will be more than happy to help you!

Other Related Steel

Latest Products

CONTACT WALDUN STEEL

Mobile:

+8618652469606

Email:

iguhongtao@gmail.com

waldun steel iso 9001 logo 300x158

Get A Quote Now !

© Copyright - WALDUN STEEL