AISI 4330 / 4330V Steel

AISI 4330 / 4330V Steel - Oil & Gas Steel | Waldun

WALDUN is one of the best AISI 4330 / 4330V Steel manufacturers and suppliers in China, you can get ound rods,square/flat bars,rollers,shafts,blocks and forging pieces with competitive price.

AISI 4330 / 4330V Steel is a general nickel-molybdenum alloy steel as per American standard which has high strength,toughness and excellent hardenability. AISI 4330 / 4330V Steel is usually supplied under quenched and tempered condition at the hardness of 24 – 29HRc.

Typical applications are for structural use, such as aircraft landing gear, power transmission gears and shafts and other structural parts.

AISI 4330 / 4330V Steel Chemical Composition

GRADE C Si Mn P S Cr Mo Ni V
4330 0.30-0.34 0.15-0.35 0.75-1.00 ≤ 0.035 ≤ 0.035 0.75-1.00 0.40-0.50 1.65-2.00 0.05-0.10

AISI 4330 / 4330V Steel SIZE & TOLERANCE & PROCESS

Shape Size(mm) Process Tolerance Length(mm)
Round Φ6-Φ50 Cold Drawn H11 3000-5800
Round Φ40-Φ300 Hot Rolled -0/+3mm 3000-10000
Round Φ120-Φ1000 Hot Forged -0/+3mm 3000-10000
Flat/Square/Block Thickness:120-800
Width:120-1500
Hot Forged -0/+3mm 500-6000

AISI 4330 / 4330V Steel HEAT TREATMENT

Normalizing For AISI 4330 / 4330V Steel
1.Nominal normalizing temperature:840-900°C
2.Hold the temperature for several hours
3.Cooling in the air

Annealing  For AISI 4330 / 4330V Steel
1.Nominal Annealing temperature:800-860°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 270

Hardening and Tempering(QT)  For AISI 4330 / 4330V Steel
1.Nominal Hardening temperature:830-865°C
2.Hold at this temperature then quench in oil
3.Tempering  as soon as possible when the temperature low to ambient temperature
4.Heat the steel carefully to a suitable temperature selected by reference to a tempering chart or table
5.The usual tempering temperature is 600°C which depending on the actual requirements
6..keep the material out of the furnace ,then cool in the air

AISI 4330 / 4330V Steel Mechanical Property( for reference only)

1.Tensile strength: 1020MPa
2.Yield point: 945MPa
3.Percentage reduction of area after fracture: 55%
4.Elongation after fracture: 13%
5.Impact test (+20°C): Transverse – 27~32J; Longitud – 45~50J

AISI 4330 / 4330V Steel DELIVERY CONDITION

1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Normalized/Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container.  above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Typcial Hardness:HRC28-32
8.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
9.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
10.Forging Ratio: minimum 4 : 1
11.Marking: Grade/Weight/Length/Size/Heat Number

AISI 4330 / 4330V Steel QUALITY CERTIFICATION

A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria