36NiCrMo16 / 1.6773 Steel
36NiCrMo16 / 1.6773 Steel Description and Application
36NiCrMo16 / 1.6773 Steel, almost equivalent to 34NiCrMo16 steel standardized according to UNI7874/7845, characterized by very high tensile strength together with good toughness. It is usable in the hardened and stress relieved state. It can harden in the air up to thicknesses equal to 90 mm. It is suitable to the manufacture of components of maximum thickness equal to 300 mm strongly stressed and even with a complicated geometry (shafts, torsion shafts, axles, levers, connecting rods, rocker arms). To improve the workability at the machines tools it can be booked with the addition of Ca or re-sulphurized (S60,1%).
The use of re-sulphurized steels involves a worsening of the tensile strength characteristics along the transversal, of the impact strength and of the fatigue strength. Advised austenitic grain dimension > 5 according to UNI 3245 (similar to ASTM E 112-82)
36NiCrMo16 / 1.6773 Steel Grades Comparison
DIN | EN | ANFOR |
1.6773 | 36NiCrMo16 | 35NCD16 |
36NiCrMo16 / 1.6773 Steel Quality Standard
EN 10083 Steels for quenching and tempering. Technical delivery conditions for alloy steels
EN 10250 Open steel die forgings for general engineering purposes. Alloy special steels
36NiCrMo16 / 1.6773 Steel Chemical Composition per EN 10083-3
GRADE | NUMBER | C | Si | Mn | P | S | Cr | Mo | Ni |
36NiCrMo16 | 1.6773 | 0.32-0.39 | ≤ 0.40 | 0.50-0.80 | ≤ 0.025 | ≤ 0.025 | 1.60-2.00 | 0.25-0.45 | 3.60-4.10 |
36NiCrMo16 / 1.6773 Steel Mechanical Properties(T=20°C if not differently stated)
Process | Diameter(mm) | Tensile Strength Rm (Mpa) | Yield Strength Rp0.2 (Mpa) | Elongation A5 (%) | Area Reduction Ratio C (%) | Impact Value Kv (J) Room Temperature | Hardness (HB) |
SOFT ANNEALED | / | 912 max | / | / | / | / | 269 max |
QUENCHED AND TEMPERED | 16 max | 1250-1450 | 1050 min | 9 min | 40 min | / | 368-424 |
QUENCHED AND TEMPERED | 16-40 | 1250-1450 | 1050 min | 9 min | 40 min | 30 min | 368-424 |
QUENCHED AND TEMPERED | 40-100 | 1100-1300 | 900 min | 10 min | 45 min | 35 min | 324-382 |
QUENCHED AND TEMPERED | 100-160 | 1000-1200 | 800 min | 11 min | 50 min | 45 min | 295-353 |
QUENCHED AND TEMPERED | 160-250 | 1000-1200 | 800 min | 11 min | 50 min | 45 min | 295-353 |
36NiCrMo16 / 1.6773 Steel HEAT TREATMENT:
- Soft Annealing: Heat to 650-680oC, cool slowly. This will produce a maximum Brinell hardness of 269.
- Normalizing:Temperature: 850-880oC.
- Hardening:Harden from a temperature of 835-865oC, 855-885oC followed by oil or quenching.
- Tempering: 550 – 650℃
36NiCrMo16 / 1.6773 Steel Forging:
Hot forming temperature: 1050-850oC.
36NiCrMo16 / 1.6773 Steel Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Page Contents
- 36NiCrMo16 / 1.6773 Steel Description and Application
- 36NiCrMo16 / 1.6773 Steel Grades Comparison
- 36NiCrMo16 / 1.6773 Steel Quality Standard
- 36NiCrMo16 / 1.6773 Steel Chemical Composition per EN 10083-3
- 36NiCrMo16 / 1.6773 Steel Mechanical Properties(T=20°C if not differently stated)
- 36NiCrMo16 / 1.6773 Steel HEAT TREATMENT:
- 36NiCrMo16 / 1.6773 Steel Forging:
- 36NiCrMo16 / 1.6773 Steel Mill′s test certificate: