20MnCr5 / 1.7149 Steel
20MnCrS5 / 1.7149 Steel manufacturers and suppliers, supplied in round rods,square/flat bars,rollers,shafts,blocks and forging pieces.
20MnCrS5 / 1.7149 Steel a Chromium-Manganese steel according to DIN standard which has tensile strength and wearing resistance after QT heat treatment.It is widely used in piston bolts, spindles, camshafts, gears, shafts and other mechanical controlling parts.
20MnCrS5 / 1.7149 Steel Chemical Composition per EN 10084 (Case Hardening Steel)
GRADE | NUMBER | C | Si | Mn | P | S | Cr |
20MnCr5 | 1.7149 | 0.17-0.22 | ≤ 0.40 | 1.10-1.40 | ≤ 0.025 | 0.020-0.040 | 1.00-1.30 |
20MnCrS5 / 1.7149 Steel Mechanical Property
Tensile strength | Yield strength | Elongation | Reduction of area |
1400Mpa | 1200MPa | 13 | 57 |
20MnCrS5 / 1.7149 Steel Related Specifications
DIN | AFNOR | BS | ASTM/SAE |
16MnCr5 | 16MC5 | 590M17 | 5115 |
20MnCr5 | 20MC5 | – | 5120 |
20MnCrS5 / 1.7149 Steel Heat Treatment & Mechanical Property
20MnCr5/20MnCrS5 | |
Normalizing,°C | 840-870 |
Annealing,°C | 650-700 |
Carburizing,°C | 880-980 |
Core Hardening,°C | 860-900 |
Case Hardening,°C | 780-820 |
Tempering,°C | 150-200 |
20MnCrS5 / 1.7149 Steel Hardness requirements for delivery conditions
Conditions | 16MnCr5/16MnCrS5 | 20MnCr5/20MnCrS5 |
Treated to improve shearability(+S) | – | ≤255 |
Soft annealed(+A) | ≤207 | ≤217 |
Treated to Hardness range(+TH) | 156-207 | 170-217 |
Treated to ferrite-pearlite structure and hardness range(+FP) | 140-187 | 152-201 |
Normalized(+N) | 138-187 | 140-201 |
20MnCrS5 / 1.7149 Steel Hardenability Limits
Distance from quenched end mm | 1.5 | 3.0 | 5.0 | 7.0 | 9.0 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 | |
16MnCr5+H 16MnCrS5+H | Min | 39 | 36 | 31 | 28 | 24 | 21 | – | – | – | – | – | – | – |
Max | 47 | 46 | 44 | 41 | 39 | 37 | 35 | 33 | 31 | 30 | 29 | 28 | 27 | |
20MnCr5+H 20MnCrS5+H | Min | 41 | 39 | 36 | 33 | 30 | 28 | 26 | 25 | 23 | 21 | – | – | – |
Max | 49 | 49 | 48 | 46 | 43 | 42 | 41 | 39 | 37 | 35 | 34 | 33 | 32 | |
16MnCr5+HH 16MnCrS5+HH | Min | 42 | 39 | 35 | 32 | 29 | 26 | 24 | 22 | 20 | – | – | – | – |
Max | 47 | 46 | 44 | 41 | 39 | 37 | 35 | 33 | 31 | 30 | 29 | 28 | 27 | |
20MnCr5+HH 20MnCrS5+HH | Min | 44 | 42 | 40 | 37 | 34 | 33 | 31 | 30 | 28 | 26 | 25 | 24 | 23 |
Max | 49 | 49 | 48 | 46 | 43 | 42 | 41 | 39 | 37 | 35 | 34 | 33 | 32 | |
16MnCr5+HL 16MnCrS5+HL | Min | 39 | 36 | 31 | 28 | 24 | 21 | – | – | – | – | – | – | – |
Max | 44 | 43 | 40 | 37 | 34 | 32 | 30 | 28 | 26 | 25 | 24 | 23 | 22 | |
20MnCr5+HL 20MnCrS5+HL | Min | 41 | 39 | 36 | 33 | 30 | 28 | 26 | 25 | 23 | 21 | – | – | – |
Max | 46 | 46 | 44 | 42 | 39 | 37 | 36 | 34 | 32 | 30 | 29 | 28 | 27 |
20MnCrS5 / 1.7149 Steel Supply Form & Size
- Round Bars: Dia.80 – 1,000mm as Forged
- Flat / Square Bars: Thickness Max.800mm
- Shafts, Rollers, Blocks: Customized or According to Drawing
- Rolled Round Bars: Dia.16 – 130mm with UT Assurance
Heat treatment: Normalizing (+N), Annealing (+A)
Surface finish:Black / Rough turned / Peeled
Page Contents
- 20MnCrS5 / 1.7149 Steel Chemical Composition per EN 10084 (Case Hardening Steel)
- 20MnCrS5 / 1.7149 Steel Mechanical Property
- 20MnCrS5 / 1.7149 Steel Related Specifications
- 20MnCrS5 / 1.7149 Steel Heat Treatment & Mechanical Property
- 20MnCrS5 / 1.7149 Steel Hardness requirements for delivery conditions
- 20MnCrS5 / 1.7149 Steel Hardenability Limits
- 20MnCrS5 / 1.7149 Steel Supply Form & Size