17CrNiMo6 / 1.6587 Steel
17CrNiMo6/1.65827 Steel is is a heat treatable, low alloy steel containing nickel, chromium and molybdenum as per DIN Germany standard which is known for its toughness and capability of developing high strength in the heat treated condition while retaining good fatigue strength. 17CrNiMo6/1.6587 Steel is widely used in heavy duty Shafts, Gears, Axles, Spindles, Couplings, Pins etc.
17CrNiMo6/1.65827 Steel Chemical Composition per DIN 17210 (Case Hardening Steels)
GRADE | NUMBER | C | Si | Mn | P | S | Cr | Mo | Ni |
17CrNiMo6 | 1.6587 | 0.15-0.20 | ≤ 0.40 | 0.40-0.60 | ≤ 0.035 | ≤ 0.035 | 1.50-1.80 | 0.25-0.35 | 1.40-1.70 |
17CrNiMo6/1.65827 Steel Size&Tolerance&Process | ||||
Shape | Size(mm) | Process | Tolerance | Length(mm) |
Round | Φ6-Φ50 | Cold Drawn | H11 | 3000-5800 |
Round | Φ40-Φ300 | Hot Rolled | -0/+3mm | 3000-10000 |
Round | Φ120-Φ1000 | Hot Forged | -0/+3mm | 3000-10000 |
Flat/Square/Block | Thickness:120-800 Width:120-1500 | Hot Forged | -0/+3mm | 500-6000 |
17CrNiMo6/1.65827 Steel Heat Treatment
Normalizing For 17CrNiMo6/1.6587
1.Nominal normalizing temperature:840-890°C
2.Hold the temperature for several hours
3.Cooling in the air
Annealing For 17CrNiMo6/1.6587
1.Nominal Annealing temperature:630-650°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 229
Hardening and Tempering(QT) For 17CrNiMo6/1.6587
1.Nominal Hardening temperature:830-865°C
2.Hold at this temperature then quench in oil
3.Tempering as soon as possible when the temperature low to ambient temperature
4.Heat the steel carefully to a suitable temperature selected by reference to a tempering chart or table
5.The usual tempering temperature is 600°C which depending on the actual requirements
6..keep the material out of the furnace ,then cool in the air
17CrNiMo6/1.65827 Steel Mechanical Property( for reference only)
1.Tensile strength: 980-1270MPa
2.Yield point: 780MPa
3.Percentage reduction of area after fracture: 40%
4.Elongation after fracture: 11%
5.Impact test (+20°C): Longitud – 45~50J
17CrNiMo6/1.65827 Steel Delivery Condition
1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Normalized/Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container. above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Typcial Hardness:HRC28-32
8.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
9.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
10.Forging Ratio: minimum 4 : 1
11.Marking: Grade/Weight/Length/Size/Heat Number
17CrNiMo6/1.65827 Steel Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria
17CrNiMo6/1.6587 Steel manufacturers and suppliers, supplied with round rods,square/flat bars,rollers,shafts,blocks and forging pieces.
Page Contents
- 17CrNiMo6/1.65827 Steel Chemical Composition per DIN 17210 (Case Hardening Steels)
- 17CrNiMo6/1.65827 Steel Size&Tolerance&Process
- 17CrNiMo6/1.65827 Steel Heat Treatment
- 17CrNiMo6/1.65827 Steel Mechanical Property( for reference only)
- 17CrNiMo6/1.65827 Steel Delivery Condition
- 17CrNiMo6/1.65827 Steel Quality Certification