1.6582 Steel| DIN 1.6582 | 34CrNiMo6
WALDUN is one of the best 1.6582 steel Manufacturers and Exporters from China, supplied with round,square,flat,block,and shaft etc. DIN 1.6582/34CrNiMo6 a heat treatable, low alloy steel which contains chromium,molybdenum and nickel as strengthening agents as per BS EN 10083-3:2006. It is known for its good strength,toughness, hardenability and capability of developing high strength in the heat treated condition while retaining good fatigue strength,but it is poor in weldability,usually this steel should be hardened and tempered before application.
1.6582 steel is used for the requirement of high strength, high toughness, large cross-sectional size and more important tempered parts, such as the drive eccentric shaft of horizontal forging machine, forging press crankshaft, etc.. Used after tempering, used to make important parts requiring good plasticity, high strength and large size. If the heavy machinery in the high load of the shaft, diameter greater than 250mm turbine shaft, blade, high load of transmission parts, fasteners, crankshaft, gears, etc.. In addition, nitriding treatment can also be used to make important parts with special performance requirements.
1.6582 Steel Supply Form & Size & Tolerance
Supply Form | Size(mm) | Process | Tolerance | |
Round | Φ6-Φ100 | Cold Drawn | Bright/Black | Best H11 |
Φ16-Φ350 | Hot Rolled | Black | -0/+1mm | |
Peeled/ground | Best H11 | |||
Φ90-Φ1000 | Hot Forged | Black | -0/+5mm | |
Rough Turned | -0/+3mm | |||
Flat/Square/Block | Thickness :120-800 | Hot Forged | Black | -0/+8mm |
Width:120-1500 | Rough Machined | -0/+3mm |
Remark:Tolerance can be customized as per requests
1.6582 Steel Chemical Composition
Standard | Grade | C | Mn | P | S | Si | Ni | Cr | Mo |
EN 10083 EN 10250 | 34CrNiMo6 | 0.30-0.38 | 0.50-0.80 | ≤ 0.025 | ≤ 0.035 | ≤ 0.04 | 1.3-1.7 | 1.3-1.7 | 0.15-0.3 |
1.6582 |
1.6582 Steel Physical Property
Density, g/cm3 | 7.85 | ||||
Specific heat capacity J/(kg.K) | 460 | ||||
Electric resistivity Ohm.mm2 /m | 0.19 | ||||
Electric conductivity Siemens.m/mm2 | 5.26 | ||||
Modulus of elasticity Gpa | 100 ℃ | 200 ℃ | 300 ℃ | 400 ℃ | 500 ℃ |
205 | 195 | 185 | 175 | ||
Thermal expansion 10^6 m/(m.K) | 100 ℃ | 200 ℃ | 300 ℃ | 400 ℃ | 500 ℃ |
11.1 | 12.1 | 12.9 | 13.5 | 13.9 |
1.6582 Steel Mechanical Property
Depth mm | 25 | 1/3 radius | 1/2 Diameter |
R Mpa | 930 | 900 | 860 |
Rp 0.2 Mpa | 828 | 750 | 730 |
A % | 18.6 | 15.4 | 12.6 |
C % | 64 | 60 | 46 |
Kv +20 ℃ J | / | / | 70/74/70 |
Kv -40 ℃ J | 110/110/118 | 48/44/45 | 25/28/25 |
Hardness HB | 279 | 271 | 264 |
Longitudinal Tesing
Forged round bar Dia 520mm,Quenched at 870 ℃ in water,tempered at 630 ℃ in air.
1.6582 Steel Forging
DIN 1.6582/34CrNiMo6 forging temperature:850 – 1100°C
1.6582 Steel Heat Treatment
- Normalizing: 850 – 880°C,Cooling in air
- Soft Annealing:650 – 680°C,Cooling in furnace,Max Hardness:248HB
- Full Annealing:830-900°C,Cooling in furnace to 300°C
- Stress relieve:450-650°C ,appr. 50 °C under tempering temperature
- Hardening:830 – 860°C,Quenching in oil
- Tempering:540 – 660°C,Cooling in air
1.6582 Steel Application
DIN 1.6582/34CrNiMo6 steel is used to make tools which requires good plasticity and high strength. It is usually selected to make the big size and important parts, such as heavy machinery axle,turbine shaft blade, high load of transmission parts, fasteners, crank shafts, gears, as well as heavily loaded parts for motor construction etc.