1.3343/HS6-5-2C High Speed Steel

1.3343 high speed steel1

1.3343/HS6-5-2C high speed steel manufacturers and suppliers, supplied in round bar,square bar,flat bar,plate,sheet and wire.

1.3343/HS6-5-2C is a tungsten-molybdenum high speed steel with a well balanced composition suitable for a wide variety of applications. It can withstand higher temperatures without losing its temper and also display high hardness,toughness and abrasion resistance.Typical applications for 1.3343/HS6-5-2C are twist drills, reamers, broaching tools, taps, milling tools, metal saws.

Chemical Composition: 1.3343 per DIN 17350 (High Speed Steel); HS6-5-2C per EN ISO 4957

GRADE NUMBER C Si Mn P S Cr Mo V W
HS6-5-2C   0.86-0.94 ≤ 0.45 ≤ 0.40 ≤ 0.030 ≤ 0.030 3.80-4.50 4.70-5.20 1.70-2.10 5.90-6.70
  1.3343 0.86-0.94 ≤ 0.45 ≤ 0.40 ≤ 0.030 ≤ 0.030 3.80-4.50 4.70-5.20 1.70-2.00 6.00-6.70

Related Specification

AISI/ASTM: M2
JIS/KS: SKH51/SKH9
UNS: T11302
ΓOCT:P6M5

Heat Treatment

Annealing

1.1.3343/HS6-5-2C must be annealed after hot working and before re-hardening.
2.Heat the temperature to 850°C at a rate of no more than 220°C per hour.
3.Hold at the temperature for one hour per inch of thickness(at least two hours).
4.Cool slowly in the furnace or in air to ambient temperature.
5.The resultant hardness achieved should be Max 248HBW or lower.’

Hardening

1.Preheat 1.3343/HS6-5-2C to 450-500°C .then up to 850-900°C.
2.Heat to the final hardening temperature of 1200-1250°C and make sure the material must be heated through.
3.Quench in warm oil or brine,and then complete the quench in air.(care must be taken at this step)
4.1.3343/HS6-5-2C high speed steel is suitable for vacuum hardening.

Tempering

1.Tempering must be done immediately after quenching.
2.Heat thoroughly and uniformly to the tempering temperature.
3.Hold at the temperature for at least two hours (one hour per inch of the total thickness).
4.Double tempering is required.

Delivery Condition

Shape:Round / Square / Flat Bars, Sheet, Plate,Wire.
Surface Condition:Black/Turning/grinding
Round bar
Diameter 1-16mm 10-50mm 50-180mm 180-300mm
Process Cold Drawn Hot Rolled Hot Forged Free Forging
Flat bar
Thickness 1-2.5mm 1.5-20mm 20-300mm
Width Max 800mm Max 800mm Max 800mm
Process Cold Drawn Hot Rolled Hot Forged

Quality Assured Supply


1.3343/HS6-5-2C high speed steel is supplied in accordance with our ISO 9001 : 2008 registration.

Latest Products

CONTACT WALDUN STEEL

Mobile:

+8618652469606

Email:

iguhongtao@gmail.com

waldun steel iso 9001 logo 300x158

Get A Quote Now !

© Copyright - WALDUN STEEL