Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
41CrS4 / 1,7039 Aço - EN 10083 | Waldun Steel

41Aço CrS4 / 1,7039 

41CrS4 1,7039 Aço

41CrS4 / 1,7039 Composição Química do Aço de acordo com EN 10083-3

 

NOTA NÚMERO C Si Mn P S Cr
41CrS4 1.7039 0,38-0,45 ≤ 0,40 0,60-0,90 ≤ 0,025 0,02-0,04 0,90-1,20

41CrS4 / 1.7039 Descrição do Aço

Aço estrutural especial.

41CrS4 / 1.7039 Aplicações de Aço

Peças de baixa e moderada tensão para veículos, motores e máquinas onde é necessária uma superfície dura e resistente ao desgaste.

Dureza como superfície endurecida cerca de 54 HRC.

41CrS4 / 1.7039 Propriedades físicas do aço (valores médios) à temperatura ambiente

Módulo de elasticidade [103 x N / mm2]: 210 Densidade [g / cm3]: 7,80

41CrS4 / 1.7039 Recozimento Macio de Aço

Aquecer a 680-720oC, resfriar lentamente na fornalha. Isso produzirá uma dureza Brinell máxima de 241.

41CrS4 / 1.7039 Normalização de Aço

Temperatura: 840-880oC.

41CrS4 / 1.7039 Endurecimento de Aço

Endureça a partir de uma temperatura de 820-860oC seguida de têmpera em óleo ou água.

41CrS4 / 1.7039 Revenido de Aço

Temperatura de revenido: 540-680oC.

41CrS4 / 1.7039 Propriedades mecânicas do aço em condição temperada e temperada

Diâmetro (mm) 0,2 tensão de prova (N / mm2) Força de tração (N / mm2) Alongamento (%) Redução (%) Energia de impacto (J)
Até 16 800 1000-1200 11 30 30
17-40 660 900-110 12 35 35
41-100 560 800-950 14 40 35

41CrS4 / 1.7039 Endurecimento do aço no teste de têmpera final

A temperatura de têmpera no teste de têmpera final é 850oC

Dureza 1,5 3 5 7 9 11 13 15 20 25 30 35 40 45 50
H max. 61 61 60 59 58 56 54 52 46 42 40 38 37 36 35
H min. 53 52 50 47 41 37 34 32 29 26 23 21 – – –
HH max. 61 61 60 59 58 56 54 52 46 42 40 38 37 36 35
HH min. 58 55 53 51 47 43 41 39 35 31 29 27 26 25 24
HL max. 58 58 57 55 52 50 47 45 40 37 34 32 31 30 29
HL min. 53 52 50 47 41 37 34 32 29 26 23 21 – – –

 41CrS4 / 1.7039 Forjamento de Aço

Temperatura de formação a quente: 1050-850oC.

Produtos Mais recentes

ENTRE EM CONTATO COM A WALDUN STEEL

Móvel:

+8618652469606

O email: