{"id":1813,"date":"2023-08-29T12:35:42","date_gmt":"2023-08-29T12:35:42","guid":{"rendered":"https:\/\/waldunsteel.com\/?post_type=portfolio&p=1813"},"modified":"2023-11-13T02:58:25","modified_gmt":"2023-11-13T02:58:25","slug":"c45r-1-1201-acier-special","status":"publish","type":"portfolio","link":"https:\/\/waldunsteel.com\/fr\/products\/c45r-1-1201-special-steel\/","title":{"rendered":"C45R \/ 1.1201 Acier sp\u00e9cial"},"content":{"rendered":"

C45R \/ 1.1201 Acier sp\u00e9cial<\/b><\/strong><\/h1>\n

\"barres<\/p>\n

L'acier sp\u00e9cial C45R \/ 1.1201 est un acier \u00e0 r\u00e9sistance moyenne fourni \u00e0 l'\u00e9tat forg\u00e9 ou normalis\u00e9. Il a une r\u00e9sistance \u00e0 la traction de 570 \u00e0 700 MPa et une plage de duret\u00e9 Brinell de 170 \u00e0 210HB. L'acier sp\u00e9cial C45R \/ 1.1201 offre de bonnes propri\u00e9t\u00e9s de r\u00e9sistance, de t\u00e9nacit\u00e9, de r\u00e9sistance \u00e0 l'usure et aux chocs \u00e0 l'\u00e9tat normalis\u00e9 ou lamin\u00e9 \u00e0 chaud. L'acier sp\u00e9cial C45R \/ 1.1201 a une faible capacit\u00e9 de durcissement \u00e0 c\u0153ur, seules les sections d'une taille d'environ 60 mm \u00e9tant recommand\u00e9es pour la trempe et le durcissement \u00e0 c\u0153ur. Cependant, il peut \u00eatre efficacement tremp\u00e9 \u00e0 la flamme ou par induction \u00e0 l'\u00e9tat normalis\u00e9 ou lamin\u00e9 \u00e0 chaud pour obtenir une duret\u00e9 de surface typique jusqu'\u00e0 HRC 58. la nitruration n'est pas recommand\u00e9e en raison du manque d'\u00e9l\u00e9ments en alliage. Cet acier peut \u00eatre facilement soud\u00e9 et usin\u00e9 \u00e0 condition que des proc\u00e9dures correctes soient suivi.<\/p>\n

C45R \/ 1.1201 Acier sp\u00e9cial FORME D'APPROVISIONNEMENT ET TAILLE<\/b><\/strong><\/h2>\n\n\n\n\n\n\n\n
Forme de fourniture<\/td>\nTaille (mm)<\/td>\nLongueur (mm)<\/td>\n<\/tr>\n
Barre ronde<\/td>\n\u03a66-\u03a61 000<\/td>\n3 000 \u00e0 10 000<\/td>\n<\/tr>\n
Barre carr\u00e9e<\/td>\n100 \u00d7 100 \u00e0 600 \u00d7 600<\/td>\n3 000 \u00e0 6 000<\/td>\n<\/tr>\n
Assiette \/ Feuille<\/td>\n\u00c9paisseur: 20-400
\nLargeur: 80-1 000<\/td>\n		2 000 \u00e0 6 000<\/td>\n<\/tr>\n
Bar plat \/ Blcoks<\/td>\n\u00c9paisseur: 120-800
\nLargeur: 120-1 500<\/td>\n		2 000 \u00e0 6 000<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

C45R \/ 1.1201 Acier sp\u00e9cial FINITION DE SURFACE ET TOL\u00c9RANCE<\/b><\/strong><\/h2>\n\n\n\n\n
Finition de surface<\/td>\nForg\u00e9 noir<\/td>\nNoir roul\u00e9<\/td>\nTourn\u00e9<\/td>\nAff\u00fbtage<\/td>\nBrillant<\/td>\nPel\u00e9<\/td>\n\u00c9tir\u00e9 \u00e0 froid<\/td>\n<\/tr>\n
Tol\u00e9rance<\/td>\n(0 \uff0c + 5 mm)<\/td>\n(0 \uff0c + 1 mm)<\/td>\n(0 \uff0c + 3 mm)<\/td>\nMeilleur h9<\/td>\nMeilleur h11<\/td>\nMeilleur H11<\/td>\nMeilleur H11<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

C45R \/ 1.1201 Acier sp\u00e9cial<\/b><\/strong>\u00a0<\/b><\/strong>Composition chimique selon EN 10083-2 (acier sp\u00e9cial)<\/b><\/strong><\/h2>\n\n\n\n\n
NOTER<\/b><\/strong><\/td>\nNUM\u00c9RO<\/b><\/strong><\/td>\nC<\/b><\/strong><\/td>\nSi<\/b><\/strong><\/td>\nMn<\/b><\/strong><\/td>\nP<\/b><\/strong><\/td>\nS<\/b><\/strong><\/td>\nCr<\/b><\/strong><\/td>\nMo<\/b><\/strong><\/td>\nNi<\/b><\/strong><\/td>\nCr + Mo + Ni<\/b><\/strong><\/td>\n<\/tr>\n
C45R<\/b><\/strong><\/td>\n1.1201 <\/b><\/strong><\/td>\n0,42-0,50<\/td>\n\u2264 0,40<\/td>\n0,50-0,80<\/td>\n\u2264 0,030<\/td>\n0,02-0,04<\/td>\n\u2264 0,40<\/td>\n\u2264 0,10<\/td>\n\u2264 0,40<\/td>\n\u2264 0,63<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

C45R \/ 1.1201 Acier sp\u00e9cial<\/b><\/strong>\u00a0<\/b><\/strong>PROPRI\u00c9T\u00c9 M\u00c9CANIQUE<\/b><\/strong><\/h2>\n\n\n\n\n\n\n
Finition de surface<\/td>\nR\u00e9sistance \u00e0 la traction Mpa<\/td>\nLimite d'\u00e9lasticit\u00e9 Mpa<\/td>\nAllongement, %<\/td>\nDuret\u00e9, HB<\/td>\n<\/tr>\n
\u00c9tir\u00e9 \u00e0 froid<\/td>\n640\u2013850<\/td>\n500-650<\/td>\n\u22658<\/td>\n190-270<\/td>\n<\/tr>\n
Lisse tourn\u00e9<\/td>\n570-700<\/td>\n300\u2013450<\/td>\n14 \u2013 30<\/td>\n170-210<\/td>\n<\/tr>\n
Lamin\u00e9 \u00e0 chaud \/ Forg\u00e9<\/td>\n570-700<\/td>\n300\u2013450<\/td>\n14 \u2013 30<\/td>\n170-210<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

C45R \/ 1.1201 Acier sp\u00e9cial<\/b><\/strong>\u00a0<\/b><\/strong>FORGER<\/b><\/strong><\/h2>\n

Temp\u00e9rature de forgeage : 1100\u00a0o<\/sup>C - 1200\u00a0o<\/sup>C, maintenez suffisamment de temps pour que l'acier soit compl\u00e8tement chauff\u00e9. Ne pas forger en dessous de la temp\u00e9rature de 850\u00b0C. L'acier AISI 1045 doit \u00eatre refroidi aussi lentement que possible \u00e0 l'air calme ou dans le sable apr\u00e8s forg\u00e9.<\/p>\n

C45R \/ 1.1201 Acier sp\u00e9cial<\/b><\/strong>\u00a0<\/b><\/strong>TRAITEMENT THERMIQUE<\/b><\/strong><\/h2>\n