Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La fonction _load_textdomain_just_in_time a été appelée de façon incorrecte. Le chargement de la traduction pour le domaine avia_framework a été déclenché trop tôt. Cela indique généralement que du code dans l’extension ou le thème s’exécute trop tôt. Les traductions doivent être chargées au moment de l’action init ou plus tard. Veuillez lire Débogage dans WordPress (en) pour plus d’informations. (Ce message a été ajouté à la version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
{"id":1778,"date":"2023-08-17T14:20:46","date_gmt":"2023-08-17T14:20:46","guid":{"rendered":"https:\/\/waldunsteel.com\/?post_type=portfolio&p=1778"},"modified":"2023-11-13T02:57:51","modified_gmt":"2023-11-13T02:57:51","slug":"41crs4-1-7039-steel","status":"publish","type":"portfolio","link":"https:\/\/waldunsteel.com\/fr\/des-produits-2\/41crs4-1-7039-acier\/","title":{"rendered":"41CrS4 \/ 1.7039 Steel"},"content":{"rendered":"

41<\/b><\/strong>CrS4 \/ 1.7039 Steel<\/b><\/strong>\u00a0<\/b><\/strong><\/h1>\n

\"41CrS4<\/p>\n

41CrS4 \/ 1.7039 Steel\u00a0Chemical Composition per EN 10083-3<\/h2>\n

\u00a0<\/b><\/strong><\/p>\n\n\n\n\n
GRADE<\/b><\/strong><\/td>\nNUMBER<\/b><\/strong><\/td>\nC<\/b><\/strong><\/td>\nSi<\/b><\/strong><\/td>\nMn<\/b><\/strong><\/td>\nP<\/b><\/strong><\/td>\nS<\/b><\/strong><\/td>\nCr<\/b><\/strong><\/td>\n<\/tr>\n
41CrS4<\/b><\/strong><\/td>\n1.7039 <\/b><\/strong><\/td>\n0.38-0.45<\/td>\n\u2264 0.40<\/td>\n0.60-0.90<\/td>\n\u2264 0.025<\/td>\n0.02-0.04<\/td>\n0.90-1.20<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

41CrS4 \/ 1.7039 Steel\u00a0Description<\/h2>\n

Special\u00a0structural\u00a0steel.<\/p>\n

41CrS4 \/ 1.7039 Steel Applications<\/h2>\n

Low\u00a0and\u00a0moderately\u00a0stressed\u00a0parts\u00a0for\u00a0vehicles,\u00a0engines\u00a0and\u00a0machines\u00a0where\u00a0hard,\u00a0wear\u00a0resisting\u00a0surface\u00a0is\u00a0needed.<\/p>\n

Hardness\u00a0as\u00a0surface\u00a0hardened\u00a0about\u00a054\u00a0HRC.<\/p>\n

41CrS4 \/ 1.7039 Steel Physical properties (average values) at ambient temperature<\/h2>\n

Modulus\u00a0of\u00a0elasticity\u00a0[103\u00a0x\u00a0N\/mm2]:\u00a0210 Density\u00a0[g\/cm3]:\u00a07.80<\/p>\n

41CrS4 \/ 1.7039 Steel Soft Annealing<\/h2>\n

Heat\u00a0to\u00a0680-720oC,\u00a0cool\u00a0slowly\u00a0in\u00a0furnace.\u00a0This\u00a0will\u00a0produce\u00a0a\u00a0maximum\u00a0Brinell\u00a0hardness\u00a0of\u00a0241.<\/p>\n

41CrS4 \/ 1.7039 Steel Normalizing<\/h2>\n

Temperatue:\u00a0840-880oC.<\/p>\n

41CrS4 \/ 1.7039 Steel Hardening<\/h2>\n

Harden\u00a0from\u00a0a\u00a0temperature\u00a0of\u00a0820-860oC\u00a0followed\u00a0by\u00a0oil\u00a0or\u00a0water\u00a0quenching.<\/p>\n

41CrS4 \/ 1.7039 Steel Tempering<\/h2>\n

Tempering\u00a0temperature:\u00a0540-680oC.<\/p>\n

41CrS4 \/ 1.7039 Steel Mechanical Properties in Quenched and Tempered Condition<\/h2>\n\n\n\n\n\n\n
Diameter\u00a0(mm)<\/td>\n0.2\u00a0proof\u00a0stress\u00a0(N\/mm2)<\/td>\nTensile\u00a0stregth\u00a0(N\/mm2)<\/td>\nElongation\u00a0(%)<\/td>\nReduction\u00a0(%)<\/td>\nImpact energy\u00a0(J)<\/td>\n<\/tr>\n
Up\u00a0to\u00a016<\/td>\n800<\/td>\n1000-1200<\/td>\n11<\/td>\n30<\/td>\n30<\/td>\n<\/tr>\n
17-40<\/td>\n660<\/td>\n900-110<\/td>\n12<\/td>\n35<\/td>\n35<\/td>\n<\/tr>\n
41-100<\/td>\n560<\/td>\n800-950<\/td>\n14<\/td>\n40<\/td>\n35<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

41CrS4 \/ 1.7039 Steel Hardenability in the end-quench test<\/h2>\n

Quenching\u00a0temperature\u00a0in\u00a0the\u00a0end-quench\u00a0test\u00a0is\u00a0850oC<\/p>\n\n\n\n\n\n\n\n\n\n
Hardness<\/td>\n1.5<\/td>\n3<\/td>\n5<\/td>\n7<\/td>\n9<\/td>\n11<\/td>\n13<\/td>\n15<\/td>\n20<\/td>\n25<\/td>\n30<\/td>\n35<\/td>\n40<\/td>\n45<\/td>\n50<\/td>\n<\/tr>\n
H\u00a0max.<\/td>\n61<\/td>\n61<\/td>\n60<\/td>\n59<\/td>\n58<\/td>\n56<\/td>\n54<\/td>\n52<\/td>\n46<\/td>\n42<\/td>\n40<\/td>\n38<\/td>\n37<\/td>\n36<\/td>\n35<\/td>\n<\/tr>\n
H\u00a0min.<\/td>\n53<\/td>\n52<\/td>\n50<\/td>\n47<\/td>\n41<\/td>\n37<\/td>\n34<\/td>\n32<\/td>\n29<\/td>\n26<\/td>\n23<\/td>\n21<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n
HH\u00a0max.<\/td>\n61<\/td>\n61<\/td>\n60<\/td>\n59<\/td>\n58<\/td>\n56<\/td>\n54<\/td>\n52<\/td>\n46<\/td>\n42<\/td>\n40<\/td>\n38<\/td>\n37<\/td>\n36<\/td>\n35<\/td>\n<\/tr>\n
HH\u00a0min.<\/td>\n58<\/td>\n55<\/td>\n53<\/td>\n51<\/td>\n47<\/td>\n43<\/td>\n41<\/td>\n39<\/td>\n35<\/td>\n31<\/td>\n29<\/td>\n27<\/td>\n26<\/td>\n25<\/td>\n24<\/td>\n<\/tr>\n
HL\u00a0max.<\/td>\n58<\/td>\n58<\/td>\n57<\/td>\n55<\/td>\n52<\/td>\n50<\/td>\n47<\/td>\n45<\/td>\n40<\/td>\n37<\/td>\n34<\/td>\n32<\/td>\n31<\/td>\n30<\/td>\n29<\/td>\n<\/tr>\n
HL\u00a0min.<\/td>\n53<\/td>\n52<\/td>\n50<\/td>\n47<\/td>\n41<\/td>\n37<\/td>\n34<\/td>\n32<\/td>\n29<\/td>\n26<\/td>\n23<\/td>\n21<\/td>\n–<\/td>\n–<\/td>\n–<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

\u00a0<\/b><\/strong>41CrS4 \/ 1.7039 Steel Forging<\/h2>\n

Hot\u00a0forming\u00a0temperature:\u00a01050-850oC.<\/p>\n<\/div><\/section><\/div>