Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La fonction _load_textdomain_just_in_time a été appelée de façon incorrecte. Le chargement de la traduction pour le domaine avia_framework a été déclenché trop tôt. Cela indique généralement que du code dans l’extension ou le thème s’exécute trop tôt. Les traductions doivent être chargées au moment de l’action init ou plus tard. Veuillez lire Débogage dans WordPress (en) pour plus d’informations. (Ce message a été ajouté à la version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
{"id":1770,"date":"2023-08-12T12:26:08","date_gmt":"2023-08-12T12:26:08","guid":{"rendered":"https:\/\/waldunsteel.com\/?post_type=portfolio&p=1770"},"modified":"2023-11-13T02:53:40","modified_gmt":"2023-11-13T02:53:40","slug":"30nicrmo16-6-1-6747-steel","status":"publish","type":"portfolio","link":"https:\/\/waldunsteel.com\/fr\/des-produits-2\/30nicrmo16-6-1-6747-acier\/","title":{"rendered":"30NiCrMo16-6 \/ 1.6747 Steel"},"content":{"rendered":"

30NiCrMo16-6 \/ 1.6747 Steel<\/b><\/strong><\/h1>\n

\"30NiCrMo16-6<\/p>\n

30NiCrMo16-6 Steel for Quenching and Tempering 1.6747 35NCD16<\/b><\/strong><\/p>\n

30NiCrMo16-6 \/ 1.6747 Stee<\/strong>l <\/strong>Application<\/strong><\/h2>\n

30NiCrMo16-6 \/ 1.6747 Steel\u00a0exhibit very good hardenability, impact resistance, load, deformation, wear and tensions resistances.<\/p>\n

Used for heavy-duty parts of engines, devices and machines, \u00a0aviation and aerospace industries, used in the\u00a0production of crankshafts, gears, shafts, bolts, heat-treated gears and piston rods, etc.<\/p>\n

30NiCrMo16-6 \/ 1.6747 Steel<\/strong>\u00a0<\/strong>Quality Standard<\/strong><\/h2>\n

-DIN EN 10083-3 Steel for quenching and tempering alloy steels.<\/p>\n

30NiCrMo16-6 \/ 1.6747 Steel<\/strong>\u00a0<\/strong>Chemical Composition per EN 10083-3<\/strong><\/h2>\n\n\n\n\n
GRADE<\/b><\/strong><\/td>\nNUMBER<\/b><\/strong><\/td>\nC<\/b><\/strong><\/td>\nSi<\/b><\/strong><\/td>\nMn<\/b><\/strong><\/td>\nP<\/b><\/strong><\/td>\nS<\/b><\/strong><\/td>\nCr<\/b><\/strong><\/td>\nMo<\/b><\/strong><\/td>\nNi<\/b><\/strong><\/td>\n<\/tr>\n
30NiCrMo16-6<\/b><\/strong><\/td>\n1.6747 <\/b><\/strong><\/td>\n0.26-0.33<\/td>\n\u2264 0.40<\/td>\n0.50-0.80<\/td>\n\u2264 0.025<\/td>\n\u2264 0.025<\/td>\n1.20-1.50<\/td>\n0.30-0.60<\/td>\n3.30-4.30<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

\u00a0<\/b><\/strong><\/p>\n

30NiCrMo16-6 \/ 1.6747 Steel<\/strong>\u00a0<\/strong>Mechanical Properties<\/strong><\/h2>\n\n\n\n\n\n\n\n\n
Heat treatment<\/td>\nDiameter
\n(mm)<\/td>\n
Tensile Strength Rm (Mpa)<\/td>\nYield Strength Rp0.2 (Mpa)<\/td>\nElongation % in 2\u2033 (%)<\/td>\nReduction Of Area (%)<\/td>\nImpact Test
\n(J)<\/td>\n<\/tr>\n
Q+T<\/td>\n16 max<\/td>\n1080-1230<\/td>\n880 min<\/td>\n10 min<\/td>\n45 min<\/td>\n\/<\/td>\n<\/tr>\n
Q+T<\/td>\n16-40<\/td>\n1080-1230<\/td>\n880 min<\/td>\n10 min<\/td>\n45 min<\/td>\n35 min<\/td>\n<\/tr>\n
Q+T<\/td>\n40-100<\/td>\n1080-1230<\/td>\n880 min<\/td>\n10 min<\/td>\n45 min<\/td>\n35 min<\/td>\n<\/tr>\n
Q+T<\/td>\n100-160<\/td>\n900-1050<\/td>\n790 min<\/td>\n11 min<\/td>\n50 min<\/td>\n35 min<\/td>\n<\/tr>\n
Q+T<\/td>\n160-250<\/td>\n900-1050<\/td>\n880 min<\/td>\n11 min<\/td>\n50 min<\/td>\n35 min<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

30NiCrMo16-6 \/ 1.6747 Steel<\/strong>\u00a0<\/strong>Heat treatment<\/strong><\/h2>\n\n\n\n\n\n\n\n\n
Process<\/td>\nTemperature<\/td>\n<\/tr>\n
Normalizing annealing<\/td>\n850 \u2013 880\u2103<\/td>\n<\/tr>\n
Softening annealing<\/td>\n650 \u2013 700\u2103<\/td>\n<\/tr>\n
Hardening<\/td>\n865 \u2013 885\u2103<\/td>\n<\/tr>\n
Tempering<\/td>\n550 \u2013 650\u2103<\/td>\n<\/tr>\n
Hardness in softened state<\/td>\n269 HB max<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

30NiCrMo16-6 \/ 1.6747 Steel<\/strong>\u00a0<\/strong>Test<\/strong><\/h2>\n

Chemical analysis, Mechnical analysis, Ultrasonic testing, Metallographic, Surface quality and dimension report.<\/p>\n

30NiCrMo16-6 \/ 1.6747 Steel<\/strong>\u00a0<\/strong>Mill\u2019s Test Certificate<\/strong><\/h2>\n

EN 10204\/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.<\/p>\n<\/div><\/section><\/div>