Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La fonction _load_textdomain_just_in_time a été appelée de façon incorrecte. Le chargement de la traduction pour le domaine avia_framework a été déclenché trop tôt. Cela indique généralement que du code dans l’extension ou le thème s’exécute trop tôt. Les traductions doivent être chargées au moment de l’action init ou plus tard. Veuillez lire Débogage dans WordPress (en) pour plus d’informations. (Ce message a été ajouté à la version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
DIN 1.0501 - Acier Waldun

DIN 1.0501 Acier

En tant qu'acier de construction au carbone de haute qualité, DIN 1.0501 est défini comme un acier non allié avec une teneur en carbone modérée de 0,35% selon les normes européennes.

L'acier DIN 1.0501 a une résistance appropriée, une bonne plasticité et de bonnes performances de traitement. Par rapport à l'acier C22, les performances de soudage sont légèrement inférieures, mais toujours acceptables. Normalement, l'acier C35 est utilisé dans un état normalisé et trempé et revenu.

L'acier DIN 1.0501 est largement utilisé dans la fabrication de diverses pièces forgées et pressées à chaud, d'aciers étirés à froid et refoulés, de tubes en acier sans soudure, de pièces dans la fabrication de machines, telles que des vilebrequins, des arbres rotatifs, des axes d'arbre, des leviers, des bielles, des poutres , manchons, roulettes Bagues, rondelles, vis, écrous, etc.

C35 Acier rond forgé à l'état normalisé

COMPOSITION CHIMIQUE DE L'ACIER DIN 1.0501

Standard Classe C Si Mn P S Cr Mo Ni
EN10083 C35/1.0501 0,32-0,39 ≤0,4 0,50-0,80 ≤0,045 ≤0,045 ≤ 0,4 ≤ 0,1 ≤ 0,4
EN10250
DIN 17200 CK35/1.1181 0,32-0,39 ≤0,4 0,50-0,80 ≤0,035 ≤0.03 – – –
COUDRE550 CK35/1.1181 0,32-0,39 ≤0,35 0,50-0,80 ≤0,035 ≤0,035 – – –

DIN 1.0501 NORMES CONCERNANT L'ACIER ET GRADE ÉQUIVALENT

Chine | GB 3077:35

États-Unis | ASTM A29:1035

Japon | JIS G4051:S35C

Royaume-Uni |BS970:080M36

France | NFA 33-101:AF55-C35

PROPRIÉTÉ PHYSIQUE DE L'ACIER DIN 1.0501

Densité, g / cm3 7,87
Point de fusion, ℃ 1395
Capacité thermique spécifique，(0~100℃),J/(kg.k) 482
Coefficient de dilatation linéaire, 10^-6/k 12.45(0-100℃)
Coefficient de Poisson 0,29
Module d'élasticité, Mpa 212213
Module de cisaillement, MPa 82080
Conductivité thermique, W/(mK) 46(100℃）

FORGE DE L'ACIER DIN 1.0501

  • Température de forgeage initiale：1200℃
  • Température finale de forgeage：800℃
  • Rapport de forgeage：au dessus de 4:1
  • Traitement post-forgeage :L'acier C35 doit refroidir lentement après avoir été forgé.

DIN 1.0501 TRAITEMENT THERMIQUE DE L'ACIER

Température critique pour le traitement thermique de l'acier DIN 1.0501

  • Ac1:724℃
  • Ac3:802℃
  • Ar1:680℃
  • Ar3:774℃

Sélection de la température pour le traitement thermique conventionnel de l'acier DIN 1.0501

  • Recuit : 850 - 880 °C, refroidissement au four, dureté inférieure à 187 HBW
  • Normalisation : 860-900 °C, refroidissement à l'air, dureté 137-197 HBW

Schéma de recuit de l'acier C35

Diagramme de normalisation de l'acier DIN 1.0501

  • Trempe : 840-880 °C, milieu : eau, huile
  • Trempe:550-660°C

Propriété mécanique de l'acier DIN 1.0501 avec état trempé et revenu

Résistance à la traction
Mpa		 Limite d'élasticité
Mpa		 Élongation
%		 Réduction de la superficie
%		 Impact Charpy-V
J
≥530 ≥315 ≥20 ≥45 ≥55

DIN 1.0501 Température de revenu de l'acier par rapport à la dureté

Classe Trempe Température de trempe, ºC
Température, ºC Dureté, HRC 150ºC 200ºC 300ºC 400ºC 500ºC 550ºC 600ºC
DIN 1.0501 860ºC 49-50 49 48 43 35 26 22 20

Courbe d'essai de trempe Jominy pour l'acier C35E

Courbe d'essai de trempe Jominy pour l'acier C35E

Trempe à 870°C

X : distance de l'extrémité trempée, en mm

Y : Dureté, HRC

3 : Niveau H

HRC-mm Taper 1 2 3 4 5 6 7 8 9 dix 11 13 15
MIN + H 58 57 55 53 49 41 34 31 28 27 26 25 24
MAX 48 40 33 24 22 20 – – – – – – –

Valeur indicative Courbe pour DIN 1.0501 Propriétés mécaniques de l'acier

Acier C35 Courbe de référence des propriétés mécaniques

X :température de revenu,oC

Y: Résistance à la traction et à la limite d'élasticité, Mpa

Z : allongement et réduction de la zone, %

CE QUE NOUS FOURNISSONS POUR L'ACIER DIN 1.0501

Barre ronde forgée à chaud : Φ80-Φ1000 mm

Barre ronde laminée à chaud : Φ16-Φ350mm

Barre carrée forgée à chaud : épaisseur maximale : 500 mm

Barre plate/Blcoks : épaisseur : 120-800 mm, largeur : 120-1500 mm

Finition de surface Forgé noir Noir roulé Tourné Affûtage Brillant Pelé Étiré à froid
Tolérance (0 ， + 5 mm) (0 ， + 1 mm) (0 ， + 3 mm) Meilleur h9 Meilleur h11 Meilleur H11 Meilleur H11

derniers produits

CONTACTER WALDUN STEEL

Mobile:

+8618652469606

E-mail:

iguhongtao@gmail.com

acier waldun logo iso 9001 300x158

Obtenez un devis maintenant!

© Copyright - WALDUN STEEL
Acier 25CrMo4acier 25crmo4qu'est-ce que l'acier rapide ou hss1.3243 / HS6-5-2-5 – Acier rapide (HSS)