Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La fonction _load_textdomain_just_in_time a été appelée de façon incorrecte. Le chargement de la traduction pour le domaine avia_framework a été déclenché trop tôt. Cela indique généralement que du code dans l’extension ou le thème s’exécute trop tôt. Les traductions doivent être chargées au moment de l’action init ou plus tard. Veuillez lire Débogage dans WordPress (en) pour plus d’informations. (Ce message a été ajouté à la version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
21CrMoV5-7 / 1.7709 Acier - EN 10269 | Acier Waldun

21CrMoV5-11_1.8070

21CrMoV5-11 / 1.8070 Acier

Composition chimique selon EN 10269

NOTER NUMÉRO C Si Mn P S Cr Mo Ni V
21CrMoV5-11 1.8070 0,17-0,25 0,30-0,60 0,30-0,60 ≤ 0,035 ≤ 0,035 1h20-1h50 1h00-13h20 ≤ 0,60 0,25-0,35

21CrMoV5-11 / 1.8070 Acier La description

Acier de construction spécial.

21CrMoV5-11 / 1.8070 Acier Applications

Vis et écrous et composants forgés pour moteurs à tige jusqu'à des températures de travail de 539 degrés maximum.

21CrMoV5-11 / 1.8070 Acier Propriétés mécaniques

Température de travail à chaud / ℃: 1100 ~ 850
Température de traitement thermique / ℃ | recuit / normalisation: 650 ~ 740
Température de traitement thermique / ℃ | trempe: 900 ~ 950 huile ou air
Température de traitement thermique / ℃ | revenu: 680 ~ 740
HBW: 205 ~ 250
(≥) | σb / MPa: 690 ~ 830
(≥) | σs / MPa: 540
(≥) | δ5 (%): 16
(≥) | AKV / J: 55

MPropriété échanique à haute température

Limite d'élasticité σ0.2≥ / MPa | 200 ℃: 510
Limite d'élasticité σ0.2≥ / MPa | 300 ℃: 481
Limite d'élasticité σ0.2≥ / MPa | 350 ℃: 461
Limite d'élasticité σ0.2≥ / MPa | 400 ℃: 431
Limite d'élasticité σ0.2≥ / MPa | 450 ℃: 402
Limite d'élasticité σ0.2≥ / MPa | 500 ℃: 373

21CrMoV5-11 / 1.8070 Acier UNEFormes disponibles  

Barre noire / barre plate / barre carrée / tuyau, / bande d'acier, / feuille

Brillant - pelé + polissage, meulage sans centre

Forgé - anneau, tube, gaine de tuyau, disques, arbre

Propriétés physiques (valeurs moyennes) à température ambiante

Module d'élasticité [103 x N / mm2]: 210 Densité [g / cm3]: 7,80 Transformation en refroidissement continu (CCT)

21CrMoV5-11 / 1.8070 Acier Recuit doux

Chauffer à 650-740 degrés, refroidir lentement.

21CrMoV5-11 / 1.8070 Acier Durcissement

Durcir à partir d'une température de 900 à 950 degrés suivie d'une trempe à l'huile ou à l'air.

21CrMoV5-11 / 1.8070 Acier Trempe

Température de revenu: 680-740 degrés.

21CrMoV5-11 / 1.8070 Acier Forging

Température de formage à chaud: 1100-850degree.