Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La función _load_textdomain_just_in_time ha sido llamada de forma incorrecta. La carga de la traducción para el dominio avia_framework se activó demasiado pronto. Esto suele ser un indicador de que algún código del plugin o tema se ejecuta demasiado pronto. Las traducciones deberían cargarse en la acción init o más tarde. Por favor, ve depuración en WordPress para más información. (Este mensaje fue añadido en la versión 6.7.0). in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
C22E / 1.1151 Acero especial - EN 10083 | Acero Waldun

C22E / 1.1151 Acero especial

¿Puedes soldar acero a prueba de estrés?

Según la norma EN10083-2: 2002, el acero especial C22E / 1.1151 debe apuntar para cumplir con ciertos niveles de resistencia y conformabilidad del acero. Prueba de tracción de conformabilidad para romper el alargamiento, dijo. El acero estructural se utiliza para llevar tal uso, en estos USOS la fuerza del acero es un estándar de diseño importante.

C22E / 1.1151 Acero especial se puede dividir en: acero aleado acero al carbono estructural acero de baja aleación acero resistente al calor, etc.

C22E / 1.1151 Acero especial Composición química según EN 10083-2 (acero especial)

CALIFICACIÓN NÚMERO C Si Minnesota PAG S Cr Mes Ni Cr + Mo + Ni
C22E 1.1151 0,17-0,24 ≤ 0,40 0,40-0,70 ≤ 0.030 ≤ 0.035 ≤ 0,40 ≤ 0,10 ≤ 0,40 ≤ 0,63

C22E / 1.1151 Acero especial Propiedades mecánicas en estado templado y revenido (+ QT)

Propiedades mecánicas para las secciones de regla (ver prEN10083-1: 2002, Anexo A) con un diámetro (d) o para productos planos truco (t) de
d ≤ 16 mm t ≤ 8 mm 16 mm <d ≤ 40 mm 8 mm <t ≤ 20 mm 40 mm <d ≤ 100 mm 20 mm <t ≤ 60 mm
Re min (MPa) 340 290
Rm (MPa) 500-650 470-620
Un min. (%) 20 22
Z min. (%) 50 50
KV min. (J)                   50                 50                   –

C22E / 1.1151 Acero especial Propiedades mecánicas en condición normalizada - (+ N)

Propiedades mecánicas para productos con un diámetro (d) o, para productos planos, truco (t) de
d ≤ 16 mm t ≤ 16 mm 16 mm <d ≤ 100 mm 16 mm <t ≤ 100 mm 100 mm <d ≤ 250 mm 100 mm <t ≤ 250 mm
Re min. (MPa) 240 210
Rm min. (MPa) 430 410
Un min. (%)                  24                 25                    –

C22E / 1.1151 Acero especial Condiciones de tratamiento térmico

Enfriamiento 0C Agente extintor Temperatura de revenido 0C Normalizando 0C
860-900 Agua o aceite Aceite o agua 550-660 880 hasta 940

Acero al carbono semiduro y resistente, fácilmente mecanizable por deformación en frío.

Soldabilidad de acero especial C22E / 1.1151:


Fácilmente soldable.

C22E / 1.1151 Endurecimiento de aceros especiales:


Extremadamente baja templabilidad, utilizado sobre todo para piezas de pequeña sección y cuando se permiten deformaciones debidas al temple por agua.

Notas:

CORRESPONDENCIA CON OTRAS NORMAS (a título meramente indicativo):

DIN 17200 AFNOR 35-551
 Cm22  XC18u