Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La función _load_textdomain_just_in_time ha sido llamada de forma incorrecta. La carga de la traducción para el dominio avia_framework se activó demasiado pronto. Esto suele ser un indicador de que algún código del plugin o tema se ejecuta demasiado pronto. Las traducciones deberían cargarse en la acción init o más tarde. Por favor, ve depuración en WordPress para más información. (Este mensaje fue añadido en la versión 6.7.0). in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
28Mn6 / 1.1170 Acero - Acero Waldun

¿Cuáles son ejemplos de acero aleado?

28Mn6 / 1.1170 Acero

El acero 28Mn6 / 1.1170 es acero al manganeso para uso a temperaturas moderadas y bajas en recipientes a presión.

Composición química según EN 10083-2

 

CALIFICACIÓN NÚMERO C Si Minnesota PAG S Cr Mes Ni Cr + Mo + Ni
28Mn6 1.1170 0,25-0,32 ≤ 0,40 1,30-1,65 ≤ 0.030 ≤ 0.035 ≤ 0,40 ≤ 0,10 ≤ 0,40 ≤ 0,63

Aplicaciones

Se utiliza para la fabricación de soldaduras de recipientes a presión que requieren una tenacidad de muesca mejorada para un servicio a temperatura inferior a la ambiente. Piezas de vehículos, máquinas y motores de baja y moderada tensión.

Propiedades mecánicas del acero 28Mn6 (1.1170)

Espesor nominal (mm): hasta 16 16 – 100 100 – 250 250 – 500 500 – 1000
Rm - Resistencia a la tracción (MPa) (+ N) 630 600 570 540 540
Espesor nominal (mm): hasta 16 16 – 100 100 – 250 250 – 500 500 – 1000
Re - Límite de elasticidad superior o
Rp0.2 - Resistencia de prueba 0.2% (MPa) (+ N)		 345 310 290 270 260
KV - Energía de impacto (J) (+ QT) + 20 °
40
Espesor nominal (mm): hasta 16 16 – 100 100 – 250
A - Min. alargamiento Lo = 5,65 √ Entonces (%) (+ N) 17 18 18
  Dureza Brinell (HBW): (+ S) 255
  Dureza Brinell (HBW): (+ A) 223

Propiedades físicas (valores medios) a temperatura ambiente

Módulo de elasticidad [103 x N / mm2]: 210

Densidad [g / cm3]: 7,83

Recocido suave

Esto producirá una dureza Brinell máxima de 223.

Normalizando

Normalización de la temperatura: 850-890 grados

Aliviar el estrés

El alivio de la tensión para eliminar las tensiones de mecanizado debe realizarse calentando a aprox. 650o C, manteniéndolo durante 1-2 horas al calor, seguido de enfriamiento por aire. Esta operación se realiza para reducir la distorsión durante el tratamiento térmico.

Endurecimiento

Endurecer a partir de una temperatura de 830-870 grados seguido de enfriamiento con agua o aceite.

Templado

Temperatura de revenido: 540-680 grados

últimos productos

CONTACTO ACERO WALDUN

Móvil:

+8618652469606

Correo electrónico:

iguhongtao@gmail.com

logotipo de acero waldun iso 9001 300x158

¡Obtenga una cotización ahora!

© Copyright - ACERO WALDUN
18CrNiMo7-6 / 1.6587 Acero18crnimo7 6 225x300Acero aleado AISI-4130Acero aleado AISI 4130