Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the translatepress-multilingual domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114

Notice: La función _load_textdomain_just_in_time ha sido llamada de forma incorrecta. La carga de la traducción para el dominio avia_framework se activó demasiado pronto. Esto suele ser un indicador de que algún código del plugin o tema se ejecuta demasiado pronto. Las traducciones deberían cargarse en la acción init o más tarde. Por favor, ve depuración en WordPress para más información. (Este mensaje fue añadido en la versión 6.7.0). in /home1/sohoweld/public_html/waldunsteel/wp-includes/functions.php on line 6114
21CrMoV5-11 / 1.8070 Acero - EN 10269 | Acero Waldun

21CrMoV5-11_1.8070

21CrMoV5-11 / 1.8070 Acero

Descripciones de productos de una línea:

  1. "Acero 21CrMoV5-11 / 1.8070: acero estructural especial diseñado para brindar durabilidad en componentes de motores de vapor de alta temperatura".
  2. "Durable y versátil, el acero 21CrMoV5-11/1.8070 es ideal para fabricar sujetadores de alta resistencia y piezas forjadas en entornos térmicos exigentes".
  3. "Diseñado para un rendimiento excepcional, el acero 21CrMoV5-11/1.8070 ofrece propiedades mecánicas superiores adecuadas para tornillos, tuercas y aplicaciones de motores de vapor hasta 539 °C".

Composición química según EN 10269

CALIFICACIÓN NÚMERO C Si Minnesota PAG S Cr Mes Ni V
21CrMoV5-11 1.8070 0,17-0,25 0,30-0,60 0,30-0,60 ≤ 0.035 ≤ 0.035 1,20-1,50 1,00-1,20 ≤ 0,60 0,25-0,35

21CrMoV5-11 / 1.8070 Acero Descripción

Acero estructural especial.

21CrMoV5-11 / 1.8070 Acero Aplicaciones

Tornillos y tuercas y componentes forjados para motores staem hasta temperaturas de trabajo de 539 grados como máximo.

21CrMoV5-11 / 1.8070 Acero Propiedades mecánicas

Temperatura de trabajo caliente / ℃: 1100 ～ 850
Temperatura de tratamiento térmico / ℃ | recocido / normalización: 650 ~ 740
Temperatura de tratamiento térmico / ℃ | temple: 900 ~ 950 aceite o aire
Temperatura de tratamiento térmico / ℃ | templado: 680 ~ 740
HBW: 205 ~ 250
(≥) | σb / MPa: 690 ～ 830
(≥) | σs / MPa: 540
(≥) | δ5 (%): 16
(≥) | AKV / J: 55

METROPropiedad echanical bajo alta temperatura

Límite elástico σ0.2≥ / MPa | 200 ℃: 510
Límite elástico σ0.2≥ / MPa | 300 ℃: 481
Límite elástico σ0.2≥ / MPa | 350 ℃: 461
Límite elástico σ0.2≥ / MPa | 400 ℃: 431
Límite elástico σ0.2≥ / MPa | 450 ℃: 402
Límite elástico σ0.2≥ / MPa | 500 ℃: 373

21CrMoV5-11 / 1.8070 Acero AFormas disponibles  

Barra negra / Barra plana / Barra cuadrada / Tubería, / Tira de acero, / Hoja

Brillante: pelado + pulido, pulido sin centros

Forjado: anillo, tubo, carcasa de tubo, discos, eje

Propiedades físicas (valores medios) a temperatura ambiente

Módulo de elasticidad [103 x N / mm2]: 210 Densidad [g / cm3]: 7.80 Transformación de enfriamiento continuo (CCT)

21CrMoV5-11 / 1.8070 Acero Recocido suave

Calentar a 650-740 grados, enfriar lentamente.

21CrMoV5-11 / 1.8070 Acero Endurecimiento

Endurecer a partir de una temperatura de 900-950 grados seguido de enfriamiento con aceite o aire.

21CrMoV5-11 / 1.8070 Acero Templado

Temperatura de revenido: 680-740 grados.

21CrMoV5-11 / 1.8070 Acero Forging

Temperatura de formación en caliente: 1100-850 grados.

últimos productos

CONTACTO ACERO WALDUN

Móvil:

+8618652469606

Correo electrónico:

iguhongtao@gmail.com

logotipo de acero waldun iso 9001 300x158

¡Obtenga una cotización ahora!

© Copyright - ACERO WALDUN